Description
Alumina grinding ball also known as: high aluminum ball, high aluminum grinding ball, high aluminum ball, alumina ball, alumina ceramic ball, high aluminum porcelain ball, corundum porcelain ball, etc
Learn about performance indicators:
The Mohs hardness is 9.0
Iron oxide content: <=0.02%
Density: >3.6g/cm3
Water absorption: <=0.01%
Bulk density (bulk density) : 1.8-2.2t/m3
Size: 0.5mm~90mm
Main application equipment:
Ball mill, vertical mixing mill (picking machine), tower mill
Alumina grinding ball refers to aluminum oxide powder as raw material, after batching, grinding, powder (pulping, mud), molding, drying, burning and other processes made into, mainly as grinding medium and widely used ball stone. Because the content of alumina is more than 92%, it is also called high aluminum ball. Appearance is white ball, diameter from 0.5-120mm.
Alumina grinding ball use: With high strength, high hardness, high wear resistance, large ratio, small volume, high temperature resistance, corrosion resistance, no pollution and other excellent characteristics are widely used in different types of ceramics, porcelain glaze, glass, chemical factory thick hard material finishing and deep processing, is the ball mill, pot mill, vibration mill and other fine grinding equipment grinding medium, Its grinding efficiency and wear resistance is much better than ordinary pebble or natural pebble.
Alumina grinding ball characteristics:
(1) The main component of the product is high quality alumina, high whiteness, has no effect on the quality of the ground material.
(2) The product adopts rolling and isostatic pressing molding, which can greatly improve the grinding efficiency, reduce the grinding time, and effectively increase the effective volume of the ball mill, thus increasing the amount of grinding materials.
(3) The product has low wear and can greatly prolong the service life of the grinding body.
(4) The product can withstand more than one thousand degrees of high temperature, acid, alkali and corrosion resistance
Physical and chemical indexes of alumina grinding ball:
Performance index 92 series 95 series
Alumina (%) 92 95
Iron oxide (%) 0.02 or less 0.02 or less
Hardness (Mohs) 9 9
Water absorption rate (%) 0.01 or less 0.01 or less
Volume density (g/cm3) 3.60 or higher 3.70 or higher
Compressive strength MPa P 2000 P 2250
Wear (per thousand) 0.10 or less 0.05 or less
color white white